Publikācija: Application of Chemical Trated Illite Clay for Development of Ceramics Products

Publikācijas veids Zinātniskais raksts, kas indeksēts Web of science un/vai Scopus datu bāzē
Pamatdarbībai piesaistītais finansējums Nav zināms
Aizstāvēšana: ,
Publikācijas valoda English (en)
Nosaukums oriģinālvalodā Application of Chemical Trated Illite Clay for Development of Ceramics Products
Pētniecības nozare 2. Inženierzinātnes un tehnoloģijas
Pētniecības apakšnozare 2.4. Ķīmijas inženierzinātne
Autori Gaida Maruta Sedmale
Artūrs Korovkins
Valdis Segliņš
Lauma Lindiņa
Atslēgas vārdi Chemical treatment, illite clay
Anotācija The chemically treatment by alkali solutions of illite clay, so-called geopolymer method, were studied to show the impact on changes of structure and crystalline phases composition of treated not dehydroxylatedilliteQuarternaryclay, as well as ceramic properties and compressive strength of sintered respective ceramic samples. The degree of activating process were followed by FTIR-spectra, X-ray diffraction and differencial thermal analysis. The low temperature ceramic product was achieved by sintering of alkali solution (KOH or NaOH 1M, 3M, 4M and 6M) activated clay samples in temperature range from 1000C to 7000C . Sintered ceramic samples were characterized by compressive strength, total porosity, bulk density and shrinkage. It is shown that treatment of the illiteQuarternary clay by KOH changes illite structure, but not destroyed.Main changes could be connected with changes of O-Al-OH grouping where O is associated with neighbour Si- layer That results into lowering of sintering temperature and development of amorphous (glassy) phase of sintered at 600-700 0C ceramic samples together with growing of total porosity. Consolidated at 6000Cceramic samples have the compressive strength ranged from16-23 N.mm2. These values increases with growing of concentration of used alkali solution as well as with temperature for NaOH treated samples and is comparable with compressive strength for the respective ceramic products sintered at 900 oC.
DOI: 10.1088/1757-899X/47/1/012056
Hipersaite: http://iopscience.iop.org/1757-899X/47/1/012056 
Atsauce Sedmale, G., Korovkins, A., Segliņš, V., Lindiņa, L. Application of Chemical Trated Illite Clay for Development of Ceramics Products. IOP Conference Series: Materials Science and Engineering, 2013, Vol.47, Iss.1, 012056.-012056.lpp. ISSN 1757-8981. e-ISSN 1757-899X. Pieejams: doi:10.1088/1757-899X/47/1/012056