Properties of Ni–Zn Ferrite Thin Films Deposited Using Spray Pyrolysis

Thin Solid Films 2012
Andris Šutka, Gundars Strīķis, Gundars Mežinskis, Andrejs Lūsis, Juris Zavickis, Jānis Kleperis, Dmitrijs Jakovļevs

Nanocrystalline, homogeneous spinel Ni1-xZnxFe2O4 thin films were deposited on glass substrates by using spray pyrolysis of metal nitrate aqueous solutions. The thickness of deposited films was below 500 nm, but crystallite size was under 30 nm. It has been shown that the DC resistivity, dielectric loss and optical band gap of deposited films are influenced by the zinc content. High DC resistivity and low dielectric losses of thin Ni1-xZnxFe2O4 films are explained by mixed n-p conductivity and nanograin structure of spray pyrolysis deposited coatings which are changing with the ratio of Ni/Zn.

Keywords
Ni–Zn ferrite; Thin film; Spray pyrolysis;
DOI
10.1016/j.tsf.2012.11.017

Šutka, A., Strīķis, G., Mežinskis, G., Lūsis, A., Zavickis, J., Kleperis, J., Jakovļevs, D. Properties of Ni–Zn Ferrite Thin Films Deposited Using Spray Pyrolysis. Thin Solid Films, 2012, 526, pp.65-69. ISSN 0040-6090. Available from: doi:10.1016/j.tsf.2012.11.017

Publication language
English (en)